Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint

The product is composed of the chlorosulfonated polyethylene rubber. Meanwhile, it contains the modified resin, leveling agent and anti-sinking agent. Besides, this paint also has the organic solvent, curing agent, flake anti-rust pigment, etc.It features great properties as：

Strong adhesion	Thick film property	Easy to apply
Good intercoat adhesion	Excellent barrier property

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Video

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Basic Technical Datasheet

Color	Brown, Gray
Gloss	Semi-gloss
Density	~1.55 Kg/L
Solid Volume	(52±2 )%
Standard Film thickness	80µm dry film thickness (about 154µm wet film thickness)
Theoretical spreading rate	4.2m²/Kg(80µm dry film thickness)
Flash Point	31℃

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Product Packaging Packaging: Part A：20 kg in a 20-liter iron bucket. Part B：4 kg in a 5-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Applicable Environment

Steel frame of chemical workshop	Metal frame around acid-alkali tank	Boiler auxiliary steel structure	Iron tower frame
Viaduct steel component	Storage rack	Steel structure of transformer cabinet	Wind turbine tower

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Finished Projects

 

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Production Process

Chlorosulfonated Polyethylene Anti-corrosive   Intermediate Paint Instructions For Use

Substrate Treatment：

All surfaces to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

Steel: Sanding to Sa2.5 (ISO8501-1:2007). It is acceptable to polish by power tools to meet at least St2.0 (ISO8501-1:2007).

Steel coated with workshop primer: make sure workshop primer surface is clean, dry and undamaged.

Coated surface: applied on clean, dry and undamaged primer only.

Instructions for Use:

Mixing：

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.

Mixing Ratio：Part A: Part B= 20:4 (by weight)

Thinner: Special thinner

Airless spray：

Nozzle tip: 0.018~0.025 inches

Spray pressure: 18~25 Mpa

Thinner ratio: 5~15% (by weight of paint)

Brush, Roller : Recommended Must achieve required thickness