Epoxy Glass Flake Finish

This product is a two-component thick film topcoat based on epoxy resin,  anti-rust filler, amine adduct curing agent.It has the following resistance characteristics:

Tough film coating	Wear resistance	Impermeable
High mechanical strength	Shock resistance	Crack resistance

Epoxy Glass Flake Finish Video

Epoxy Glass Flake Finish Basic Technical Datasheet

Color	Customized
Gloss	Glossy on rough surface
Density	~1.2Kg/L(after mixing)
Hardness	Epoxy glass flake curing agent
Solid Volume	(60±2 )%
Standard Film thickness	100um dry film thickness  (about 167um wet film thickness)
Theoretical spreading rate	5m²/Kg (100um dry film thickness)
Full Cure	(23±2℃) 7d
Flash Point	27℃

Epoxy Glass Flake Finish Product Packaging Packaging: Part A 20kg in a 20-liter iron bucket. Part B 5kg in a 6-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Epoxy Glass Flake Finish Applicable Environment

Storage Tank	Reactor	Reaction Tank	Sewage Tank
Heat Exchanger	Laboratory	Pickling Tank	Distillation Column

Epoxy Glass Flake Finish Compatibility

	Product	Thickness
Paint:	Epoxy Glass Flake Anti-rust Paint	2*100 µm (dry film thickness)
Topcoat:	Epoxy Glass Flake Finish	2*50um (dry film thickness)

Epoxy Glass Flake Finish Finished Projects

 

Epoxy Glass Flake Finish Production Process

Epoxy Glass Flake Finish 

Instructions For Use

Substrate Treatment：

All surfaces to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

For bare steel, it shall be sandblasted to reach Sa2.5(iso8501-1:2007) standard. Depending on the environment of the non-immersed part, grinding with power tools is acceptable but shall at least reach St2(iso8501-1:2007) standard.

For shop primed steel, the shop primer shall be clean, dry and approved.

For surface painted coatings, this product can apply only to clean, dry and good compatible primer.

Instructions for Use:

• Mixing:

First add the white water and stir it evenly, then add blue water and stir.

Caution: Do not add blue and white water at the same time to avoid burning.

• Mixing Ratio

Part A: Accelerator: Initiator=20:0.4:0.4 (by weight)

• Thinner:

Exclusive thinner (It is recommended to add small amount or not add thinner.)

• Scraping：

Scrap it to form a uniform and flat putty film. After the surface is dry, roll it back and forth with a ceramic roller (moistened with toluene) to form a flat and compact fish scale structure (scales in the same direction)