YMS COATINGS
Gray, Iron red
Flat
~1.42Kg/L (after mixing)
25℃
(50±2 )%
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally speaking, if the temperature is below 10 ℃, it needs 30 min induction time; if the temperature is over 10℃, it needs 15 min induction time.
Part A: Part B = 25:3 (by weight)
3.52m²/Kg (100µm dry film thickness)
Availability: | |
---|---|
Epoxy Zinc Phosphate Anti-rust Paint
This product is a two-component epoxy paint composed of epoxy resin and polyamide curing agent. Meanwhile, the paint contains zinc phosphate corrosion inhibitor pigment.It has the following resistance characteristics:
|
|
|
Color | Gray, Iron red |
Gloss | Flat |
Density | ~1.42Kg/L (after mixing) |
Hardness | Epoxy zinc phosphate curing agent |
Solid Volume | (50±2 )% |
Standard Film thickness | 100µm dry film thickness (about 200µm wet film thickness) |
Theoretical spreading rate | 3.52m²/Kg (100µm dry film thickness) |
Full Cure | (23±2℃) 7d |
Flash Point | 25℃ |
![]() | Epoxy Zinc Phosphate Anti-rust Paint Product PackagingPackaging: Part A 25kg in a 20-liter iron bucket. Part B 3kg in a 4-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using. |
![]() | ![]() | ![]() | ![]() |
Container | Steel beam | Pipeline | Compressor housing |
Product | Thickness | |
Primer: | Epoxy Zinc Phosphate Anti-rust Primer | 2*50 µm (dry film thickness) |
Paint: | Epoxy Mica Iron Oxide Paint | 2*50 µm (dry film thickness) |
Topcoat: | Acrylic Polyurethane Finish Paint | 2*40 µm (dry film thickness) |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Substrate Treatment:
All surfaces to be coated shall be clean, dry and without contaminants. The surface shall be evaluated and treated according to ISO8504 standard.
Bare steel: Sand blasting to meet Sa2.5 (ISO8501-1:2007) standard. Depending on the environment of non-submerged part, it is acceptable to polish by power tools to meet at least St2.0 (ISO8501-1:2007) standard.
Steel coated with workshop primer: make sure workshop primer surface is clean, dry
and undamaged.
Coated surface: applied on clean, dry, undamaged and compatible primer only.
Instructions for Use:
Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally speaking, if the temperature is below 10 ℃, it needs 30 min induction time; if the temperature is over 10℃, it needs 15 min induction time.
Mixing Ratio
Part A: Part B = 25:3 (by weight)
Thinner:
Epoxy paint thinner
Airless spray:
Nozzle tip: 0.018~0.027 inches
Spray pressure: 15~18Mpa
Thinner ratio: 5~15% (by weight of paint)
BrushRoller:
Recommended
Must achieve required thickness
![]() | |||
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Epoxy Zinc Phosphate Anti-rust Paint
This product is a two-component epoxy paint composed of epoxy resin and polyamide curing agent. Meanwhile, the paint contains zinc phosphate corrosion inhibitor pigment.It has the following resistance characteristics:
|
|
|
Color | Gray, Iron red |
Gloss | Flat |
Density | ~1.42Kg/L (after mixing) |
Hardness | Epoxy zinc phosphate curing agent |
Solid Volume | (50±2 )% |
Standard Film thickness | 100µm dry film thickness (about 200µm wet film thickness) |
Theoretical spreading rate | 3.52m²/Kg (100µm dry film thickness) |
Full Cure | (23±2℃) 7d |
Flash Point | 25℃ |
![]() | Epoxy Zinc Phosphate Anti-rust Paint Product PackagingPackaging: Part A 25kg in a 20-liter iron bucket. Part B 3kg in a 4-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using. |
![]() | ![]() | ![]() | ![]() |
Container | Steel beam | Pipeline | Compressor housing |
Product | Thickness | |
Primer: | Epoxy Zinc Phosphate Anti-rust Primer | 2*50 µm (dry film thickness) |
Paint: | Epoxy Mica Iron Oxide Paint | 2*50 µm (dry film thickness) |
Topcoat: | Acrylic Polyurethane Finish Paint | 2*40 µm (dry film thickness) |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Substrate Treatment:
All surfaces to be coated shall be clean, dry and without contaminants. The surface shall be evaluated and treated according to ISO8504 standard.
Bare steel: Sand blasting to meet Sa2.5 (ISO8501-1:2007) standard. Depending on the environment of non-submerged part, it is acceptable to polish by power tools to meet at least St2.0 (ISO8501-1:2007) standard.
Steel coated with workshop primer: make sure workshop primer surface is clean, dry
and undamaged.
Coated surface: applied on clean, dry, undamaged and compatible primer only.
Instructions for Use:
Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally speaking, if the temperature is below 10 ℃, it needs 30 min induction time; if the temperature is over 10℃, it needs 15 min induction time.
Mixing Ratio
Part A: Part B = 25:3 (by weight)
Thinner:
Epoxy paint thinner
Airless spray:
Nozzle tip: 0.018~0.027 inches
Spray pressure: 15~18Mpa
Thinner ratio: 5~15% (by weight of paint)
BrushRoller:
Recommended
Must achieve required thickness
![]() | |||
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |