Epoxy Mica Iron Oxide Intermediate Paint

The two-component high-solid product is composed of epoxy resin and polyamie curing agent.It has the following characteristics：

Excellent adhesion	Good flexibility	Impact resistance
Low‑VOC	Good abrasion‑resistance

Epoxy Mica Iron Oxide Intermediate Paint Video

Epoxy Mica Iron Oxide Intermediate Paint Basic Technical Datasheet

Color	Gray, Bronzing
Gloss	Flat
Density	~1.6Kg/L (after mixing)
Hardness	Curing agent for epoxy paint
Solid Volume	(75±2 )%
Standard Film thickness	150um dry film thickness  (about 200um wet film thickness)
Theoretical spreading rate	3.13m²/Kg (150um dry film thickness)
Full cure	(23±2℃ )7d
Flash Point	39℃

Epoxy Mica Iron Oxide Intermediate Paint Product Packaging Packaging: part A：24 kg in a 20-liter iron bucket. part B：4 kg in a 5-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Epoxy Mica Iron Oxide Intermediate Paint Applicable Environment

Port Machinery	Power Transmission Towers	Bridges	Chemical Plants
Offshore Platforms	Power Plants	Workshop Steel Structures	Storage Tanks

Epoxy Mica Iron Oxide Intermediate Paint Compatibility

	Product	Thickness
Primer:	Epoxy Zinc Rich Primer	2*40um  (dry film thickness)
Midcoat:	Epoxy Mica Iron Oxide Intermediate Paint	2*75um  (dry film thickness)
Topcoat:	Acrylic Polyurethane Finish	2*40um  (dry film thickness)

Epoxy Mica Iron Oxide Intermediate Paint Finished Projects

Epoxy Mica Iron Oxide Intermediate Paint Production Process

Epoxy Mica Iron Oxide Intermediate Paint Instructions For Use

Substrate Treatment：

All surfaces to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

Steel: Sanding to Sa2.5 (ISO8501-1:2007). It is acceptable to polish by power tools to meet at least St2.0 (ISO8501-1:2007).

Steel coated with workshop primer: make sure workshop primer surface is clean, dry and undamaged.

Coated surface: applied on clean, dry and undamaged primer only.

Instructions for Use:

• Mixing:

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally, if the temperature below 10 ℃, it needs 30 min induction time; if the temperature over 10℃, it needs 15 min induction time.

• Mixing ratio：

Part A: Part B = 24:4 (by weight)

• Thinner:

Epoxy paint thinner

• Airless spray:

Nozzle tip: 0.018~0.027inches

Spray pressure: 15~18Mpa

Thinner ratio: 5~15% (by weight of paint)

• Brush、Roller：

Recommended Must achieve required thickness