Fluorocarbon Topcoat

This two-component product, cured at room temperature, is composed of fluorocarbon resin.It has the following characteristics：

Gloss and color retention	Strong adhesion	Good scratch resistance
Easy to clean	Excellent anti-pollution resistance

Fluorocarbon Topcoat Video

Fluorocarbon Topcoat Basic Technical Datasheet

Color	Customized
Gloss	Flat
Density	~1.30Kg/L(after mixing)
Hardness	Exclusive curing agent for fluorocarbon paint
Solid Volume	(50±2 )%
Standard Film thickness	80um dry film thickness  (about 160um wet film thickness)
Theoretical spreading rate	4.8m²/Kg (80um dry film thickness)
Full Cure	(23±2℃ )7d
Flash Point	31℃

Fluorocarbon Topcoat  Product Packaging Packaging: part A：20 kg in a 20-liter iron bucket. part B：4 kg in a 5-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Fluorocarbon Topcoat Applicable Environment

High-speed railway station	Airport	Stadium	Bridge
Photovoltaic bracket	Wind turbine tower	Substation	Dock

Fluorocarbon Topcoat Compatibility

	Product	Thickness
Primer:	Epoxy Zinc Rich Primer	2*40 µm (dry film thickness)
Midcoat:	Epoxy Mica Iron Oxide Paint	2*50 µm (dry film thickness)
Topcoat:	Fluorocarbon Topcoat	2*40um (dry film thickness)

Fluorocarbon Topcoat Finished Projects

Fluorocarbon Topcoat Production Process

Fluorocarbon Topcoat Instructions For Use

Substrate Treatment：

All surfaces to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

Steel: Sanding to Sa2.5 (ISO8501-1:2007). It is acceptable to polish by power tools to meet at least St2.0 (ISO8501-1:2007).

Steel coated with workshop primer: make sure workshop primer surface is clean, dry and undamaged.

Coated surface: applied on clean, dry and undamaged primer only.

Instructions for Use:

• Mixing:

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.

• Mixing ratio:

Part A: Part B=20:4(by weight)

• Thinner:

Exclusive thinner for fluorocarbon paint

• Airless spray:

Nozzle tip: 0.017~0.023 inches

Spray pressure: 15~18Mpa

Thinner ratio: 0~15% (by weight of paint)

• BrushRoller:

Recommended

Must achieve required thickness