W61-1200
YMS
Gray, Black
Glossy
~1.32Kg/L (after mixing)
27℃
(45±2 )%
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you to mix the paint well. The mixture is cured 30minutes no less than 10℃ while15 minutes over 10 ℃.
Part A: Part B= 20:2(by weight)
5.68m²/Kg (60um dry film thickness)
Availability: | |
---|---|
W61-1200 Silicone Heat Resistant Paint
This ambient curing two components paint is composed of organosilicon resin, special heat-resistant and anti-corrosive pigments, fillers, additives and curing agent, etc., and it has the following outstanding characteristics:
|
|
|
|
|
|
Color | Gray, Black |
Gloss | Glossy |
Density | ~1.32Kg/L(after mixing) |
Hardness | Heat-resistant curing agent |
Solid Volume | (45±2 )% |
Standard Film thickness | 60um dry film thickness (about 133um wet film thickness) |
Theoretical spreading rate | 5.68m²/Kg (60um dry film thickness) |
Full cure | (23±2℃) 24h |
Flash Point | 27℃ |
![]() | W61-1200 Silicone Heat Resistant Paint Product PackagingPackaging: part A:20kg in a 20-liter iron bucket. part B:2kg in a 4-liter iron bucket. Shelf Life: Part A:12 months,Part B:6 months If exceeding shelf life, the products shall be tested before using. |
![]() | ![]() | ![]() | ![]() |
Metallurgy | Aerospace | Electric Power | Oil industry |
Product | Thickness | |
Primer: | Silicone Heat Resistant Primer 1200℃ | 2*40 µm (dry film thickness) |
Topcoat: | Silicone Heat Resistant Paint 1200℃ | 2*30um (dry film thickness) |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Substrate Treatment:
The surface to be coated shall be clean, dry and free from contaminations. Also, the surface shall be evaluated and handled according to ISO8504 standard.
Bare steel: sandblasting to Sa2.5(IOS8501-1:2007). For the non-soaking site, acceptable for power tool grinding, but at least reach St2(IOS8501-1:2007).
Steel painted shop primer: apply to clean, dry, intact and approved primer.
Painted surface: only apply to clean, dry and intact compatible primer.
Instructions for Use:
Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you to mix the paint well. The mixture is cured 30minutes no less than 10℃ while15 minutes over 10 ℃.
Mixing ratio:
Part A: Part B= 20:2 (by weight)
Thinner:
Exclusive thinner for heat-resistant paint
Airless spray:
Nozzle tip: 0.017~0.023 inches
Spray pressure: 15~18Mpa
Thinner ratio: 5~15% (by weight of paint)
Brush、Roller:
Recommended for small areas only. Must achieve required thickness.
Roller coater
Not recommended.
![]() | |||
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
W61-1200 Silicone Heat Resistant Paint
This ambient curing two components paint is composed of organosilicon resin, special heat-resistant and anti-corrosive pigments, fillers, additives and curing agent, etc., and it has the following outstanding characteristics:
|
|
|
|
|
|
Color | Gray, Black |
Gloss | Glossy |
Density | ~1.32Kg/L(after mixing) |
Hardness | Heat-resistant curing agent |
Solid Volume | (45±2 )% |
Standard Film thickness | 60um dry film thickness (about 133um wet film thickness) |
Theoretical spreading rate | 5.68m²/Kg (60um dry film thickness) |
Full cure | (23±2℃) 24h |
Flash Point | 27℃ |
![]() | W61-1200 Silicone Heat Resistant Paint Product PackagingPackaging: part A:20kg in a 20-liter iron bucket. part B:2kg in a 4-liter iron bucket. Shelf Life: Part A:12 months,Part B:6 months If exceeding shelf life, the products shall be tested before using. |
![]() | ![]() | ![]() | ![]() |
Metallurgy | Aerospace | Electric Power | Oil industry |
Product | Thickness | |
Primer: | Silicone Heat Resistant Primer 1200℃ | 2*40 µm (dry film thickness) |
Topcoat: | Silicone Heat Resistant Paint 1200℃ | 2*30um (dry film thickness) |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Substrate Treatment:
The surface to be coated shall be clean, dry and free from contaminations. Also, the surface shall be evaluated and handled according to ISO8504 standard.
Bare steel: sandblasting to Sa2.5(IOS8501-1:2007). For the non-soaking site, acceptable for power tool grinding, but at least reach St2(IOS8501-1:2007).
Steel painted shop primer: apply to clean, dry, intact and approved primer.
Painted surface: only apply to clean, dry and intact compatible primer.
Instructions for Use:
Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you to mix the paint well. The mixture is cured 30minutes no less than 10℃ while15 minutes over 10 ℃.
Mixing ratio:
Part A: Part B= 20:2 (by weight)
Thinner:
Exclusive thinner for heat-resistant paint
Airless spray:
Nozzle tip: 0.017~0.023 inches
Spray pressure: 15~18Mpa
Thinner ratio: 5~15% (by weight of paint)
Brush、Roller:
Recommended for small areas only. Must achieve required thickness.
Roller coater
Not recommended.
![]() | |||
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |