Organic Silicone High Temperature Anti-corrosive Finish Paint

This ambient curing two components paint is composed of organosilicon resin, special heat-resistant and anti-corrosive pigments, fillers, additives and curing agent, etc., and it has the following outstanding characteristics:

Can withstand 800°C long-term.	Anti-corrosion	Resistant to chemical atmosphere
Anti-aging	Waterproof	Rapidly adapt to temperature differences

Organic Silicone High Temperature Anti-corrosive Finish Paint Video

Organic Silicone High Temperature Anti-corrosive Finish Paint 

Basic Technical Datasheet

Color	Gray, Black
Gloss	Glossy
Density	~1.37Kg/L(after mixing)
Hardness	High temperature resistance curing agent
Solid Volume	(45±2 )%
Standard Film thickness	150um dry film thickness  (about 300um wet film thickness)
Theoretical spreading rate	2.63m²/Kg (150um dry film thickness)
Full cure	(27±2℃) 24h
Flash Point	27℃

Organic Silicone High Temperature Anti-corrosive Finish Paint Packaging Packaging: part A：20KG part B：4KG Shelf Life: Part A：12 months，Part B：6 months If exceeding shelf life, the products shall be tested before using.

Organic Silicone High Temperature Anti-corrosive Finish Paint 

Applicable Environment

Metallurgy	Aerospace	Petroleum industry	High-temperature pipeline

Organic Silicone High Temperature Anti-corrosive Finish Paint Compatibility

	Product	Thickness
Primer:	Silicone Heat Resistant Primer 800℃	2*40 µm (dry film thickness)
Topcoat:	Silicone Heat Resistant Paint 800℃	2*30um (dry film thickness)

Organic Silicone High Temperature Anti-corrosive Finish Paint Finished Projects

 

Organic Silicone High Temperature Anti-corrosive Finish Paint Production Process

Organic Silicone High Temperature Anti-corrosive Finish Paint

Instructions For Use

Substrate Treatment：

The surface to be coated shall be clean, dry and free from contaminations. Also, the surface shall be evaluated and handled according to ISO8504 standard.

Bare steel: sandblasting to Sa2.5(IOS8501-1:2007). For the non-soaking site, acceptable for power tool grinding, but at least reach St2(IOS8501-1:2007).

Steel painted shop primer: apply to clean, dry, intact and approved primer.

Painted surface: only apply to clean, dry and intact compatible primer.

Instructions for Use:

• Mixing:

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you to mix the paint well. The mixture is cured 30minutes no less than 10℃ while15 minutes over 10 ℃.

• Mixing ratio:

Part A: Part B= 20:4 (by weight)

• Thinner:

Exclusive thinner for heat-resistant paint

• Airless spray:

Nozzle tip: 0.017~0.023 inches

Spray pressure: 15~18Mpa

Thinner ratio: 5~15% (by weight of paint)

• Brush、Roller:

Recommended for small areas only.  Must achieve required thickness.

• Roller coater

Not recommended.

Organic Silicone High Temperature Anti-corrosive Finish Paint 

Company Introduction

Organic Silicone High Temperature Anti-corrosive Finish Paint Exhibitions