Waterborne Heat-resistant Finish (200 ℃）

This paint is composed of waterborne silicon resin, pigments with resistance to heat and corrosion, titanium dioxide, talcum powder, additives, film forming agent, etc.It has the following resistance characteristics:

Low VOC

Outstanding temperature resistance

Excellent physical properties

Waterborne Heat-resistant Finish (200 ℃） Video

Waterborne Heat-resistant Finish (200 ℃） Basic Technical Datasheet

Color	Customized
Gloss	Flat
Density	~1.2 Kg/L
Solid Volume	(35±2 )%
Standard Film thickness	60um dry film thickness  (about 171um wet film thickness)
Theoretical spreading rate	4.86m²/Kg (60um dry film thickness)
Adhesion	Level 1

Waterborne Heat-resistant Finish (200 ℃） Product Packaging Packaging: 20kg in a 20-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Waterborne Heat-resistant Finish (200 ℃） Applicable Environment

Drying tunnel	Equipment	Exhaust pipe	Boiler

Waterborne Heat-resistant Finish (200 ℃） Compatibility

	Product	Thickness
Primer:	Waterborne Heat-resistant Primer	2*40 µm (dry film thickness)
Topcoat:	Waterborne Heat-resistant Finish	2*30um (dry film thickness)

Waterborne Heat-resistant Finish (200 ℃） Finished Projects

 

Waterborne Heat-resistant Finish (200 ℃） Production Process

Waterborne Heat-resistant Finish (200 ℃） Instructions For Use

Substrate Treatment：

The surface to be coated shall be clean, dry, firm and free from contaminations. Also, the surface shall be evaluated and handled according to ISO8504 standard.

Painted surface: only apply to clean, dry and intact compatible primer.

Instructions for Use:

• Mixing:

Ready to use

• Thinner:

Clean water

• Airless spray:

Nozzle tip: 0.017~0.023 inches

Spray pressure: 15~18Mpa

Thinner ratio: 0~10% (by weight of paint)

• BrushRoller:

Recommended

Must achieve required thickness