Chlorosulfonated Polythene Anti-corrosive Finish

This product is a two-component product based on chlorosulfonated polythene rubber, leveling agent, anti-settling agent, anti-rust pigment and organic solvent, curing agent, etc.It features great properties as： 

Excellent aging resistance

Acid and alkali resistance

Moisture resistance

Chlorosulfonated Polythene Anti-corrosive Finish Basic Technical Datasheet

Color	Customized
Density	~1.28Kg/L
Solid Volume	(45±2 )%
Standard Film thickness	60um dry film thickness  (about 133um wet film thickness)
Theoretical spreading rate	5.85m²/Kg (60um dry film thickness)
Flash Point	31℃

Chlorosulfonated Polythene Anti-corrosive Finish Product Packaging Packaging: Part A 20 kg in a 20-liter iron bucket. Part B 4 kg in a 4-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Chlorosulfonated Polythene Anti-corrosive Finish Applicable Environment

Acid and alkali tank	Bridge	Container	Storage rack
Pipe rack steel structure	Power plant steel structure	Port	Viaduct steel component

Chlorosulfonated Polythene Anti-corrosive Finish Finished Projects

 

Chlorosulfonated Polythene Anti-corrosive Finish Production Process

Chlorosulfonated Polythene Anti-corrosive Finish Instructions For Use

Substrate Treatment：

All surface to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

For bare steel, it shall be sandblasted to reach Sa2.5(iso8501-1:2007) standard. Depending on the environment of the non-immersed part, grinding with power tools is acceptable but shall at least reach St2(iso8501-1:2007) standard.

For shop primed steel, the shop primer shall be clean, dry and approved.

For surface painted coatings, this product can apply only to clean, dry and good compatible primer.

Instructions for Use:

Mixing：

Add the curing agent into the main paint and stir it evenly before use.

Mixing ratio：Part A: Part B= 20:4

Thinner: Exclusive thinner

Airless spray：

Nozzle tip: 0.018~0.025 inches

Spray pressure: 18~25 Mpa

Thinner ratio: 0~15% (by weight of paint)

Brush, Roller : Recommended Must achieve required thickness