High Chlorinated Polyethylene Iron-red Primer

This product is composed of  chlorosulfonated polyethylene, epoxy resin, plasticizer, iron oxide red, rust-resistant pigment, etc.It has the following resistance characteristics:

Excellent rust resistance	High dry film hardness
Corrosion resistance	Water resistance	strong adhesion

High Chlorinated Polyethylene Iron-red Primer Basic Technical Datasheet

Color	Iron red
Gloss	Flat
Density	~1.5Kg/L
Solid Volume	(48±2 )%
Standard Film thickness	60um dry film thickness  (about 125um wet film thickness)
Theoretical spreading rate	5.3m²/Kg (60um dry film thickness)
Flash Point	31℃

High Chlorinated Polyethylene Iron-red Primer Product Packaging Packaging: 20KG are packaged in a 20L iron drum. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

High Chlorinated Polyethylene Iron-red Primer Applicable Environment

Chemical Pipeline	Bridge	Steel Tower	Street Light Pole
Guardrail	Steam Pipeline	Storage Tank	Port Facilities

High Chlorinated Polyethylene Iron-red Primer

 Compatibility

	Product	Thickness
Primer:	HCPE Iron-red Primer	2*30 µm (dry film thickness)
Paint:	HCPE Mica Iron Oxide Intermediate Paint	2*40 µm (dry film thickness)
Topcoat:	HCPE Finish Paint	2*30 µm (dry film thickness)

High Chlorinated Polyethylene Iron-red Primer

 Finished Projects

 

High Chlorinated Polyethylene Iron-red Primer

 Production Process

High Chlorinated Polyethylene Iron-red Primer

 Instructions For Use

Substrate Treatment：

Instructions for Use:

• Mixing:

Ready to use

• Thinner:

Exclusive thinner

• Airless spray：

Nozzle tip: 0.018~0.025 inches

Spray pressure: 18~25Mpa

Thinner ratio: 5~15% (by weight of paint)

• Brush, Roller：

Recommended Must achieve required thickness