High Chlorinated Polythene Anti-corrosive Finish

This product is based on high chlorinated polythene resin.It has the following resistance characteristics:

Acid resistance	Oil resistance	High-temperature resistance
Resistance to temperature change	Fast drying	High adhesion

High Chlorinated Polythene Anti-corrosive Finish Video

High Chlorinated Polythene Anti-corrosive Finish Basic Technical Datasheet

Color	Customized
Gloss	Flat
Density	~1.4Kg/L
Solid Volume	(44±2 )%
Standard Film thickness	60um dry film thickness (about 136um wet film thickness)
Theoretical spreading rate	5.23m²/Kg (80um dry film thickness)
Flash Point	31℃

High Chlorinated Polythene Anti-corrosive Finish Product Packaging Packaging: 20/22kg in a 20-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

High Chlorinated Polythene Anti-corrosive Finish Applicable Environment

Storage tank	Concrete storage tank	Pharmaceutical workshop	Sewage treatment tank
Bridge guardrail	Wharf steel structure	Workshop steel beam	Outdoor motor equipment

High Chlorinated Polythene Anti-corrosive Finish Compatibility

	Product	Thickness
Primer:	High Chlorinated Polythene Anti-rust Primer	2*40 µm (dry film thickness)
Topcoat:	High Chlorinated Polythene Anti-corrosive Finish	2*30um (dry film thickness)

High Chlorinated Polythene Anti-corrosive Finish Finished Projects

 

High Chlorinated Polythene Anti-corrosive Finish Production Process

High Chlorinated Polythene Anti-corrosive Finish Instructions For Use

Substrate Treatment：

All surface to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

For bare steel, it shall be sandblasted to reach Sa2.5(iso8501-1:2007) standard. Depending on the environment of the non-immersed part, grinding with power tools is acceptable but shall at least reach St2(iso8501-1:2007) standard.

For shop primed steel, the shop primer shall be clean, dry and approved.

For surface painted coatings, this product can apply only to clean, dry and good compatible primer.

Instructions for Use:

• Mixing:

Ready to use

• Thinner:

High chlorinated polythene thinner

• Airless spray:

Nozzle tip: 0.017~0.023 inches

Spray pressure: 15~18Mpa

Thinner ratio:0~10% (by weight of paint)

• BrushRoller:

Recommended

Must achieve required thickness