Inorganic Zinc-rich Primer

This product is composed of alkyl silicate solution, ultrafine metal powder, color pigment, various additives, etc. It features great properties as：

Cathodic protection	Water resistance	High temperature resistance
Weather resistance	Excellent environmental performance

Inorganic Zinc-rich Primer Video

Inorganic Zinc-rich Primer Basic Technical Datasheet

Color	Gray
Gloss	Flat
Density	~2.1Kg/L
Solid Volume	(45±2 )%
Standard Film thickness	60um dry film thickness  (about 222um wet film thickness)
Theoretical spreading rate	3.57m²/Kg (100um dry film thickness)
Flash Point	35℃

Inorganic Zinc-rich Primer Product Packaging Packaging: Part A 24 kg in a 20-liter iron bucket. Part B 6 kg in a 8-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Inorganic Zinc-rich Primer Applicable Environment

Port facilities	Bridges	Transformer housing	Transmission tower

Inorganic Zinc-rich Primer Finished Projects

 

Inorganic Zinc-rich Primer Production Process

Inorganic Zinc-rich Primer Instructions For Use

Substrate Treatment：

All surfaces to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

Steel: Sanding to Sa2.5 (ISO8501-1:2007). It is acceptable to polish by power tools to meet at least St2.0 (ISO8501-1:2007).

Steel coated with workshop primer: make sure workshop primer surface is clean, dry and undamaged.

Coated surface: applied on clean, dry and undamaged primer only.

Instructions for Use:

Mixing：

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally, if the temperature below 10 ℃, it needs 30 min induction time; if the temperature over 10℃, it needs 15 min induction time.

Mixing ratio：

Part A: Part B = 24:6 (by weight)

Thinner: Inorganic exclusive thinner

Airless spray：

Nozzle tip: 0.017~0.023inches

Spray pressure: 15~18Mpa

Thinner ratio: 5~15% (by weight of paint)

Brush, Roller : Recommended Must achieve required thickness