Inorganic Zinc Silicate Shop Primer

This two-component product is prepared by alkyl silicate solution, ultrafine metal powder, colorful pigments, various additives and solvent.  This product is designed as the maintenance primer for shot-blasted or sand-blasted steel, with the maintenance period up to 7~10 months.It features great properties as：

Excellent impact resistance	Strong wind erosion resistance	Weldable
Cuttable	Good cathodic protection performance

Inorganic Zinc Silicate Shop Primer Video

Inorganic Zinc Silicate Shop Primer Basic Technical Datasheet

Color	Gray
Gloss	No gloss
Density	~1.62Kg/L(after mixing)
Hardness	Inorganic curing agent
Solid Volume	(45±2 )%
Standard Film thickness	60um dry film thickness  (about 133um wet film thickness)
Theoretical spreading rate	4.62m²/Kg (100um dry film thickness)
Full cure	(23±2 ℃) 24h
Flash Point	18℃

Inorganic Zinc Silicate Shop Primer Product Packaging Packaging: Part A 24 kg in a 20-liter iron bucket. Part B 6 kg in a 8-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Inorganic Zinc Silicate Shop Primer Applicable Environment

Bridge steel structure	Iron tower	Port crane	Offshore platform

Inorganic Zinc Silicate Shop Primer Finished Projects

 

Inorganic Zinc Silicate Shop Primer Production Process

Inorganic Zinc Silicate Shop Primer Instructions For Use

Substrate Treatment：

The surface to be coated shall be clean, dry and free from contaminations. Also, the surface shall be evaluated and treated according to ISO8504 standard.

Bare steel: sandblasting to reach Sa2.5(IOS8501-1:2007). For the non-soaking site, acceptable for power tool grinding, at least reach St2(IOS8501-1:2007).

Steel with shop primer: only apply to clean, dry, sound and approved shop primer.

Painted surface: only apply to clean, dry and intact compatible primer.

Instructions for Use:

Mixing：

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.

Mixing ratio：

Part A: Part B = 24:6 (by weight)

Thinner: Thinner for inorganic zinc silicate shop primer

Airless spray：

Nozzle tip: 0.025~0.031inches

Spray pressure: 18~28Mpa

Thinner ratio: 5~15% (by weight of paint)

Brush, Roller : Recommended Must achieve required thickness

Inorganic Zinc Silicate Shop Primer Company Introduction

Inorganic Zinc Silicate Shop Primer Exhibitions