This one-component product, mainly composed of waterborne fluorocarbon resin with excellent performance.It has the following resistance characteristics:

Low VOC	Excellent weather resistance	Durability
Easy to clean	Good gloss retention	Corrosion resistance

Waterborne Fluorocarbon Finish Video

Waterborne Fluorocarbon Finish Basic Technical Datasheet

Color	Customized
Gloss	Flat,Matt
Density	~1.2 Kg/L
Solid Volume	(45±2 )%
Standard Film thickness	80um dry film thickness  (about 177um wet film thickness)
Theoretical spreading rate	4.68m²/Kg (40um dry film thickness)
Full cure	48h

Waterborne Fluorocarbon Finish Product Packaging Packaging: 20kg in a 20-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Waterborne Fluorocarbon Finish Applicable Environment

Solar panel mounting bracket	Pipeline	Concrete surface	Ships

Waterborne Fluorocarbon Finish Compatibility

	Product	Thickness
Primer:	Waterborne Epoxy Primer	2*40 µm (dry film thickness)
Midcoat:	Waterborne Epoxy Intermediate Paint	2*40 µm (dry film thickness)
Topcoat:	Waterborne Fluorocarbon Finish	2*40um (dry film thickness)

Waterborne Fluorocarbon Finish Finished Projects

 

Waterborne Fluorocarbon Finish Production Process

Waterborne Fluorocarbon Finish Instructions For Use

Substrate Treatment：

All the impurities such as the floating dust, dust, oil contaminations shall be removed to keep the surface clean and dry.

Instructions for Use:

• Mixing:

Ready to use

• Thinner:

Clean water

• Airless spray:

Nozzle tip: 0.017~0.023 inches

Spray pressure: 15~18Mpa

Thinner ratio: 0~10% (by weight of paint)

• BrushRoller:

Recommended

Must achieve required thickness