Epoxy Glass Flake Finish

This product is a two-component thick film topcoat based on epoxy resin,  anti-rust filler, amine adduct curing agent.It has the following characteristics：

Excellent toughness	High wear resistance	High permeability
High mechanical strength	Excellent seismic resistance

Epoxy Glass Flake Finish Video

Epoxy Glass Flake Finish Basic Technical Datasheet

Color	Customized
Gloss	Glossy on rough surface
Density	~1.2Kg/L(after mixing)
Hardness	Epoxy glass flake curing agent
Solid Volume	(60±2 )%
Standard Film thickness	100um dry film thickness  (about 167um wet film thickness)
Theoretical spreading rate	5m²/Kg (100um dry film thickness)
Full Cure	(23±2℃ )7d
Flash Point	27℃

Epoxy Glass Flake Finish Product Packaging Packaging: part A：20 kg in a 20-liter iron bucket. part B：5 kg in a 6-liter iron bucket. Shelf Life: 12 months If exceeding shelf life, the products shall be tested before using.

Epoxy Glass Flake Finish Applicable Environment

Chimney	Reactor	Storage tank	Port
Offshore platform	Pipeline	Sewage treatment equipment	Dust removal equipment

Epoxy Glass Flake Finish Compatibility

	Product	Thickness
Primer:	Epoxy Glass Flake Anti-rust Paint	2*100 µm (dry film thickness)
Topcoat:	Epoxy Glass Flake Finish	2*50um (dry film thickness)

Epoxy Glass Flake Finish Finished Projects

Epoxy Glass Flake Finish Production Process

Epoxy Glass Flake Finish Instructions For Use

Substrate Treatment：

All surface to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

For bare steel, it shall be sandblasted to reach Sa2.5(iso8501-1:2007) standard. Depending on the environment of the non-immersed part, grinding with power tools is acceptable but shall at least reach St2(iso8501-1:2007) standard.

For shop primed steel, the shop primer shall be clean, dry and approved.

For surface painted coatings, this product can apply only to clean, dry and good compatible primer.

Instructions for Use:

• Mixing:

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well. Generally, if the temperature is below 10℃, it needs 30 min induction time; If the temperature is over 10℃, it needs 15 min induction time.

• Mixing ratio:

Part A: Part B=20:5

• Thinner:

Exclusive paint thinner

• Airless spray:

Nozzle tip: 0.020~0.028 inches

Spray pressure: 15~18Mpa

Thinner ratio: 0~15% (by weight of paint)

• BrushRoller:

Recommended

Must achieve required thickness