Waterborne Epoxy Mica Iron Oxide Primer | Corrosion Resistant Coating

  • ED-31

  • Gray

  • Flat

  • ~1.45Kg/L

  • (40±2 )%

  • Level 1

  • Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.

  • Part A: Part B = 20:5

  • 3.45m²/Kg (80um dry film thickness)

Availability:
facebook sharing button
twitter sharing button
line sharing button
wechat sharing button
linkedin sharing button
pinterest sharing button
whatsapp sharing button
sharethis sharing button



Waterborne Epoxy Mica Iron Oxide Intermediate Paint


It is a two-component waterborne product composed of water-soluble modified epoxy resin with high-performance, imported waterborne amine curing agent, anti-rust pigment, micaceous iron oxide, anti-corrosive agent and various additives.It has the following resistance characteristics:

  • Low VOC

  • Abrasion resistance

  • Impact resistance

  • Salt spray resistance

  • Weather resistance

  • Good compatibility




Waterborne Epoxy Mica Iron Oxide Intermediate Paint Video






Waterborne Epoxy Mica Iron Oxide Intermediate Paint 

Basic Technical Datasheet



Color

Iron red

Gloss

Flat

Density

~1.3Kg/L

Solid Volume

(40±2 )%

Standard Film thickness

80um dry film thickness (about 200um wet film thickness)

Theoretical spreading rate


3.85m²/Kg (80um dry film thickness)

Adhesion

Level 1

01


Waterborne Epoxy Mica Iron Oxide Intermediate Paint Product Packaging

Packaging:

part A:20kg in a 20-liter iron bucket.

part B:5kg in a 6-liter iron bucket.

Shelf Life:

Part A:12 months,Part B:12 months

If exceeding shelf life, the products shall be tested before using.




Waterborne Epoxy Mica Iron Oxide Intermediate Paint 

Applicable Environment


7 5 3 4

Storage tank

Pipe rack

Chemical pipeline

Container

6 6 2 8
Gas holder Steel structure

Mechanical equipment

Bridge



Waterborne Epoxy Mica Iron Oxide Intermediate Paint Compatibility




Product Thickness

Primer:

Waterborne Epoxy Iron-red Primer


2*40 µm (dry film thickness)

Midcoat:

Waterborne Epoxy Mica Iron Oxide Intermediate Paint

2*40 µm (dry film thickness)

Topcoat:

Waterborne Epoxy Anti-corrosive Finish

2*40um (dry film thickness)



Waterborne Epoxy Mica Iron Oxide Intermediate Paint 

Finished Projects


8-9 10 11

 


Waterborne Epoxy Mica Iron Oxide Intermediate Paint 

Production Process


4-1 4-2 4-3



Waterborne Epoxy Mica Iron Oxide Intermediate Paint 

Instructions For Use



Substrate Treatment:

All surface to be coated shall be clean and dry. The surface shall be evaluated and treated according to ISO8504 standard.

For bare steel, it shall be sandblasted to reach Sa2.5(iso8501-1:2007) standard. Depending on the environment of the non-immersed part, grinding with power tools is acceptable but shall at least reach St2(iso8501-1:2007) standard.

For shop primed steel, the shop primer shall be clean, dry and approved.

For surface painted coatings, this product can apply only to clean, dry and good compatible primer.

Instructions for Use:

  • Mixing:

Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.

  • Thinner:

Clean water

  • Airless spray:

Nozzle tip: 0.017~0.023 inches

Spray pressure: 15~18Mpa

Thinner ratio:0~10% (by weight of paint)

  • BrushRoller:

Recommended

Must achieve required thickness





Waterborne Epoxy Mica Iron Oxide Intermediate Paint 

Company Introduction


8-1
6-1 6-2 6-3 6-4



Waterborne Epoxy Mica Iron Oxide Intermediate Paint Exhibitions


7-1 7-2 7-3
7-4 7-5 7-6








Previous: 
Next: 
Apply Our Best Quotation
Apply Our Best Quotation
If you have any questions about our products, reach out to YMS Paint customer service team.
    inquiry@jsbj88.com
   +86-18015818726
  +86-519-85506198

Products

Application

Quick Links

© COPYRIGHT 2024 CHANGZHOU YMS NEW MATERIALS TECHNOLOGY CO., LTD. ALL RIGHTS RESERVED.