FC-63
YMS
Gray
No Gloss
~1.92Kg/L (after mixing)
27℃
(45±2 )%
Part A: Part B= 30:3 (by weight)
2.93m²/Kg (80um dry film thickness)
Availability: | |
---|---|
Waterborne Zinc-rich Epoxy Primer
This two-component product is mainly composed of epoxy resin, zinc powder, auxiliaries, waterborne amine curing agent and deionized water.and it has the following outstanding characteristics:
|
|
|
Color | Gray, |
Gloss | Flat |
Density | 60% Zinc: ~1.95Kg/L (after mixing) 70% Zinc: ~2.30Kg/L (after mixing) 80% Zinc; ~2.4Kg/L (after mixing) |
Curing agent | Curing agent for waterborne epoxy paint |
Solid Volume | (60±2 )% |
Standard Film thickness | 80um dry film thickness (about 133um wet film thickness) |
Theoretical spreading rate | 3.2m²/Kg (80um dry film thickness, 60% zinc) 2.80m²/Kg (80um dry film thickness, 70% Zinc) 2.70m²/Kg (80um dry film thickness, 80% Zinc) |
![]() | Waterborne Zinc-rich Epoxy Primer Product PackagingPackaging: part A:20kg in a 20-liter iron bucket. part B:4kg in a 5-liter iron bucket. Shelf Life: Part A:12 months,Part B:12 months If exceeding shelf life, the products shall be tested before using. |
![]() | ![]() | ![]() | ![]() |
Bridges | oil tanks | Ships | Gas storage tanks |
Product | Thickness | |
Primer: | Waterborne Zinc-rich Epoxy Primer | 2*40 µm (dry film thickness) |
Paint: | Waterborne Epoxy Intermediate Paint | 60um (dry film thickness) |
Topcoat: | Waterborne Epoxy Finish | 2*40 µm (dry film thickness) |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Substrate Treatment:
The surface to be coated shall be clean, dry and free from contaminations. Also, the surface shall be evaluated and handled according to ISO8504 standard.
Painted surface: only apply to clean, dry and intact compatible primer.
Instructions for Use:
Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.
Thinner:
Clean water
Airless spray:
Nozzle tip: 0.025~0.031 inches
Spray pressure: 18~28Mpa
Thinner ratio: 0~10% (by weight of paint)
Brush、Roller:
Recommended Must achieve required thickness.
![]() | |||
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Waterborne Zinc-rich Epoxy Primer
This two-component product is mainly composed of epoxy resin, zinc powder, auxiliaries, waterborne amine curing agent and deionized water.and it has the following outstanding characteristics:
|
|
|
Color | Gray, |
Gloss | Flat |
Density | 60% Zinc: ~1.95Kg/L (after mixing) 70% Zinc: ~2.30Kg/L (after mixing) 80% Zinc; ~2.4Kg/L (after mixing) |
Curing agent | Curing agent for waterborne epoxy paint |
Solid Volume | (60±2 )% |
Standard Film thickness | 80um dry film thickness (about 133um wet film thickness) |
Theoretical spreading rate | 3.2m²/Kg (80um dry film thickness, 60% zinc) 2.80m²/Kg (80um dry film thickness, 70% Zinc) 2.70m²/Kg (80um dry film thickness, 80% Zinc) |
![]() | Waterborne Zinc-rich Epoxy Primer Product PackagingPackaging: part A:20kg in a 20-liter iron bucket. part B:4kg in a 5-liter iron bucket. Shelf Life: Part A:12 months,Part B:12 months If exceeding shelf life, the products shall be tested before using. |
![]() | ![]() | ![]() | ![]() |
Bridges | oil tanks | Ships | Gas storage tanks |
Product | Thickness | |
Primer: | Waterborne Zinc-rich Epoxy Primer | 2*40 µm (dry film thickness) |
Paint: | Waterborne Epoxy Intermediate Paint | 60um (dry film thickness) |
Topcoat: | Waterborne Epoxy Finish | 2*40 µm (dry film thickness) |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
Substrate Treatment:
The surface to be coated shall be clean, dry and free from contaminations. Also, the surface shall be evaluated and handled according to ISO8504 standard.
Painted surface: only apply to clean, dry and intact compatible primer.
Instructions for Use:
Mixing:
Use the power mixer to mix the main paint evenly, and then as you stir it, you add the hardener until you get to mix well.
Thinner:
Clean water
Airless spray:
Nozzle tip: 0.025~0.031 inches
Spray pressure: 18~28Mpa
Thinner ratio: 0~10% (by weight of paint)
Brush、Roller:
Recommended Must achieve required thickness.
![]() | |||
![]() | ![]() | ![]() | ![]() |
![]() | ![]() | ![]() |
![]() | ![]() | ![]() |